性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 |
熔体流动速率 | 240℃/10.0kg | ISO 1133 | 10 | g/10min |
比重 |
|
ASTM D-792 |
1.06 |
g/cm3 |
|
ISO 1183 | |||||
模具收缩率 | 流动 | ASTM D-955 | 0.4-0.7 | % | |
机械性能 | 拉伸模量 | ISO 527-2/1 | 2800 | MPa | |
抗张屈服强度 |
|
ASTM D-638 | 49.0 | MPa | |
ISO 527-2/50 | 53.0 | ||||
断裂伸长率 |
|
ASTM D-638 | 22 |
% |
|
ISO 527-2/50 | 10 | ||||
弯曲模量 | ASTM D-790 | 2400 | MPa | ||
弯曲屈服强度 |
|
ASTM D-790 | 77.0 |
MPa |
|
ISO 178 | 83.0 | ||||
简支梁缺口冲击强度 |
23℃ | ISO 179/1eA | 15 | KJ/m2 | |
悬壁梁缺口冲击强度 | 23℃,3.20mm | ASTM D-256 | 186 | J/m | |
23℃,12.7mm | 167 | ||||
洛氏硬度 | ASTM D-785 | 115 | R-scale | ||
热性能 |
热变形温度 |
1.80MPa,未退火,6.40mm | ASTM D-648 | 98.0 |
℃ |
1.80MPa,未退火 | ISO 75-2/A | 92.0 | |||
阻燃等级 | UL94 | HB |