ABS SH610S韩国LG化学挤出成型高冲击优异表面
面议
http://rysujiao.cn.qiyeku.com挤出成型高冲击优异表面（18024445500）
|
性能项目
|
测试条件 |
测试方法 |
数据单位 |
测试数据 |
|
http://rysujiao.cn.qiyeku.com |
|
|
|
|
|
比重 |
|
ASTM D792 |
- |
1.04 |
|
模具收缩率 |
|
ASTM D955 |
% |
0.4~0.7 |
|
熔融指数 |
220℃/10kg |
ASTM D1238 |
g/10min |
1 |
|
吸水率 |
23℃, 24hrs |
ASTM D570 |
% |
|
|
机械性能 |
|
|
|
|
|
拉伸强度，3.2mm |
|
ASTM D638 |
|
|
|
@屈服 |
50mm/min |
|
kg/cm 2 |
360 |
|
伸长率，3.2mm |
|
ASTM D638 |
|
|
|
@屈服 |
50mm/min |
|
% |
|
|
@断裂 |
50mm/min |
|
% |
35 |
|
拉伸模数，3.2mm |
1mm/min |
ASTM D638 |
kg/cm 2 |
|
|
抗弯强度，3.2mm |
15mm/min |
ASTM D790 |
kg/cm 2 |
580 |
|
抗弯模数，3.2mm |
15mm/min |
ASTM D790 |
kg/cm 2 |
20,000 |
|
IZOD缺口冲击强度，6.4mm |
|
ASTM D256 |
|
|
|
(Notched) |
23℃ |
|
kg·cm/cm |
36 |
|
|
-30℃ |
|
kg·cm/cm |
|
|
IZOD缺口冲击强度，3.2mm |
|
ASTM D256 |
|
|
|
(Notched) |
23℃ |
|
kg·cm/cm |
42 |
|
|
-30℃ |
|
kg·cm/cm |
|
|
http://rysujiao.cn.qiyeku.com |
R-Scale |
ASTM D785 |
- |
94 |
|
热性能 |
|
|
|
|
|
热变形温度, 6.4mm |
|
ASTM D648 |
|
|
|
（未退火） |
18.6kg |
|
℃ |
87 |
|
|
4.6kg |
|
℃ |
|
|
维卡软化点 |
|
ASTM D1525 |
|
|
|
|
5kg, 50℃/h |
|
℃ |
94 |
|
阻燃等级 |
|
UL94 |
|
|
|
相对温度指数 |
|
UL 746B |
|
|
|
电气特性 |
|
|
℃ |
|
|
有冲击条件下 |
|
|
℃ |
|
|
无冲击条件下 |
|
|
℃ |
|
|
电气特性 |
|
|
|
|
|
相比漏电起痕指数(CTI) |
Solution A |
IEC 60112 |
Volts |
|
|
表面电阻率 |
|
IEC 60093 |
Ohm |
|
|
体积电阻率 |
23℃ |
ASTM D257 |
Ohm·m |
|
|
耐电弧性 |
23℃ |
ASTM D495 |
Ohm·cm |